Chemical quenching of positronium in Fe2O3/Al2O3 catalysts

Fe₂O₃/Al₂O₃ catalysts were prepared by solid state reaction method using α-Fe₂O₃ and γ-Al₂O₃ nano powders. The microstructure and surface properties of the catalyst were studied using positron lifetime and coincidence Doppler broadening annihilation radiation measurements. The positron lifetime spectrum shows four components. The two long lifetimes τ₃ and τ₄ are attributed to positronium annihilation in two types of pores distributed inside Al₂O₃ grain and between the grains, respectively. With increasing Fe₂O₃ content from 3 wt% to 40 wt%, the lifetime τ₃ keeps nearly unchanged, while the longest lifetime τ₄ shows decrease from 96 ns to 64 ns. Its intensity decreases drastically from 24% to less than 8%. The Doppler broadening S parameter shows also a continuous decrease. Further analysis of the Doppler broadening spectra reveals a decrease in the p-Ps intensity with increasing Fe₂O₃ content, which rules out the possibility of spin-conversion of positronium. Therefore the decrease of τ₄ is most probably due to the chemical quenching reaction of positronium with Fe ions on the surface of the large pores.