Effect of NaAlO2 concentrations on microstructure and corrosion resistance of Al2O3/ZrO2 coatings formed on zirconium by micro-arc oxidation

In this study, Al₂O₃/ZrO₂ composite coatings were prepared on Zr substrates by micro-arc oxidation (MAO) in the NaAlO₂-containing electrolytes, and the effect of NaAlO₂ concentration on the microstructure, bond strength, microhardness and corrosion resistance of coatings was systematically investigated. The study reveals that the adequate NaAlO₂ in the electrolyte (>0.2 M) is essential to the formation of needle-like α-Al₂O₃ in the coatings, and the amount of α-Al₂O₃ rises with the increase of the NaAlO₂ concentration. m-ZrO₂ and t-ZrO₂ are present in all of the coatings, but their relative amount largely depends on the amount of Al₂O₃. It is also found that as the NaAlO₂ concentration increases from 0.2 to 0.3 M, the coating becomes denser and thicker, and its bond strength, maximum microhardness and corrosion resistance increases as well. The coating formed at 0.3 M NaAlO₂ demonstrates the highest bond strength of 52 MPa, the maximum microhardness of 1600 Hv_0.2N and the superior corrosion resistance. However, the overhigh concentration of NaAlO₂ (0.35 M) is found harmful to the coating's microstructure and properties.