Chemical spray pyrolysis deposition and characterization of p-type CuCr1−xMgxO2 transparent oxide semiconductor thin films

A chemical spray pyrolysis technique for deposition of p-type Mg-doped CuCrO₂ transparent oxide semiconductor thin films using metaloorganic precursors is described. As-deposited films contain mixed spinel CuCr₂O₄ and delafossite CuCrO₂ structural phases. Reduction in spinel CuCr₂O₄ fraction and formation of highly crystalline films with single phase delafossite CuCrO₂ structure is realized by annealing at temperatures ?700 °C in argon. A mechanism of synthesis of CuCrO₂ films involving precursor decomposition, oxidation and reaction between constituent oxides in the spray deposition process is presented. Post-annealed CuCr_0.93Mg_0.07O₂ thin films show high (?80%) visible transmittance and sharp absorption at band gap energy with direct and indirect optical band gaps 3.11 and 2.58 eV, respectively. Lower (∼450 °C) substrate temperature formed films are amorphous and yield lower direct (2.96 eV) and indirect (2.23 eV) band gaps after crystallization. Electrical conductivity of CuCr_0.93 Mg_0.07O₂ thin films ranged 0.6-1 S cm⁻¹ and hole concentration ∼2×10¹⁹ cm⁻³ determined from Seebeck analysis. Temperature dependence of conductivity exhibit activation energies ∼0.11 eV in 300-470 K and ∼0.23 eV in ?470 K region ascribed to activated conduction and grain boundary trap assisted conduction, respectively. Heterojunction diodes of the structure Au/n-(ZnO)/p-(CuCr_0.93Mg_0.07O₂)/SnO₂ (TCO) were fabricated which show potential for transparent wide band gap junction device.