Photoluminescence of (Ba1−xEux)Si6N8O (0.005≤x≤0.2) phosphors

Eu²⁺-doped BaSi₆N₈O phosphors (Ba_1−xEu_xSi₆N₈O, 0.005≤x≤0.2) were synthesized by gas-pressure sintering of the powder mixture of BaCO₃, Si₃N₄, and Eu₂O₃ at 1750 °C under 0.5 MPa N₂. The fired powder consists of a major BaSi₆N₈O phase and a trace amount of impurity phases. The structural result of the BaSi₆N₈O powder, refined by the Rietveld method, agrees well with that of single crystals. A wide blue luminescence band peaking at about 500 nm is observed in BaSi₆N₈O:Eu²⁺, upon excitation with the ultraviolet light of 310 nm. Although Eu is covalently bonded to six nearest neighbor nitrogen atoms, the luminescence of Eu²⁺ is not significantly redshifted but shows a very narrow excitation spectrum at high energies. The origin of the short-wavelength luminescence is mainly ascribed to a small crystal-field splitting as a result of extremely long distances between europium and nitrogen ligands in BaSi₆N₈O:Eu²⁺.