Influence of annealing temperature on the photoluminescence property of ZnO thin film covered by TiO2 nanoparticles |
|
| Authors: | Linhua Xu Hua Shen Rihong Zhu |
| Institution: | a College of Math and Physics, Physics Experiment Center, Nanjing University of Information Science and Technology, Nanjing 210044, China b Institute of Electronic Engineering and Photo-electric Technology, Nanjing University of Science and Technology, Nanjing 210094, China c Department of Applied Physics, Nanjing University of Science and Technology, Nanjing 210094, China |
| Abstract: | In this work, ZnO thin films covered by TiO2 nanoparticles (labeled as TiO2-ZnO thin films) were prepared by electron beam evaporation. The influence of annealing temperature on the photoluminescence property of the samples was studied. The structures and surface morphologies of the samples were analyzed by X-ray diffraction (XRD) and atomic force microscope, respectively. The photoluminescence was used to investigate the fluorescent properties of the samples. The measurement results show that the ultraviolet emission of ZnO thin films is largely enhanced after they are covered by TiO2 nanoparticles, while the green emission is suppressed. However, when the annealing temperature is relatively high (≥500 °C), the intensity of ultraviolet emission drops off and a violet emission peak along with a blue emission peak appears. This is probably connected with the atomic interdiffusion between TiO2 nanoparticles and ZnO thin film. Therefore, selecting a suitable annealing temperature is a key factor for obtaining the most efficient ultraviolet emission from TiO2-ZnO thin films. |
| Keywords: | ZnO thin film TiO2-nanoparticle capping Photoluminescence FRET |
| 本文献已被 ScienceDirect 等数据库收录！ | |