Irreversible helix rearrangement from Cis‐transoid to Cis‐cisoid in poly(p‐n‐hexyloxyphenylacetylene) induced by heat‐treatment in solid phase

Polymerization of p‐n‐hexyloxyphenylacetylene (pHPA) by using a Rh(norbornadine)Cl]₂‐triethylamine catalyst was carried out at room temperature to afford stereoregular helical poly(p‐n‐hexyloxyphenylacetylene)s (PpHPAs). When ethanol and n‐hexane were used as polymerization solvents, a bright yellow PpHPAs, poly( Y ) with M_n = 8.5 × 10⁴ and its purple red polymer, poly( R ) with M_n = 5.3 × 10⁴ were obtained in 95% yields and 84% yields, respectively. Diffuse reflective UV–vis spectra of poly( Y ) and poly( R ) in solid phase showed different broad absorption peaks at 445 and 575 nm, respectively. X‐Ray diffraction patterns of poly( Y ) and poly( R ) showed typical columnar structures assignable to cis‐transoid and cis‐cisoid structures, respectively, which were also supported by molecule mechanics calculation. Poly( Y ) was irreversibly transformed to a reddish‐black polymer, poly( Y‐B ), which columnar diameter was nearly the same as that of poly( R ). Further, poly( Y ) showed an exothermic peak in the differential scanning calorimetry trace at 80 °C for 1 h in N₂ gas. Thus, these findings suggest a thermally irreversible rearrangement from an unstable cis‐transoid form, poly( Y ) with a stretched cis‐transoid helix to a stable cis‐cisoid form, poly( R ), with a contracted cis‐cisoid helix in the solid phase to give poly( Y → B ) with the cis‐cisoid form. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012