Structures and luminescence properties of Yb3＋ in the double perovskites Ba2YB＇O6 （B＇=Ta5＋, Nb5＋） phosphors

The Yb³⁺ doped Ba₂YB'O₆ (B'=Ta⁵⁺, Nb⁵⁺) were prepared by high temperature solid-state reaction method, their structures were determined by x-ray diffraction and refined by Rietveld method. The diffuse reflection absorption, excitation and emission spectra of Yb³⁺:Ba₂YB'O₆ (B'=,Ta⁵⁺, Nb⁵⁺) were measured at room temperature. Under the excitation of ultraviolet light, these phosphors exhibit broad charge transfer band emissions of TaO₆ or NbO₆ centre with large Stokes shift. The Yb³⁺ doped into these hosts are situated at Y³⁺ sites of cubic symmetry (O_h). The experimental energy levels of Yb³⁺ in Ba₂YTaO₆ and Ba₂YNbO₆ were determined by photoluminescence and diffuse reflection absorption spectra. Their wavefunctions and theoretical energy levels were obtained by diagonalising the Hamiltonian matrix. The experimental energy levels were fitted by Levenberg--Marquardt iteration algorithm to determine crystal field parameters. Then, the magnetic-pole transition line strengths of Yb³⁺:Ba₂YB'O₆(B'=Ta⁵⁺, Nb⁵⁺) from (²F_5/2)Γ₈^- to the low-energy states were calculated.

Structures and luminescence properties of Yb3+ in the double perovskites Ba2YB'O6 (B'=Ta5+, Nb5+) phosphors

The Yb³⁺ doped Ba₂YB'O₆ (B'=Ta⁵⁺, Nb⁵⁺) were prepared by high temperature solid-state reaction method, their structures were determined by x-ray diffraction and refined by Rietveld method. The diffuse reflection absorption, excitation and emission spectra of Yb³⁺:Ba₂YB'O₆ (B'=,Ta⁵⁺, Nb⁵⁺) were measured at room temperature. Under the excitation of ultraviolet light, these phosphors exhibit broad charge transfer band emissions of TaO₆ or NbO₆ centre with large Stokes shift. The Yb³⁺ doped into these hosts are situated at Y³⁺ sites of cubic symmetry (O_h). The experimental energy levels of Yb³⁺ in Ba₂YTaO₆ and Ba₂YNbO₆ were determined by photoluminescence and diffuse reflection absorption spectra. Their wavefunctions and theoretical energy levels were obtained by diagonalising the Hamiltonian matrix. The experimental energy levels were fitted by Levenberg--Marquardt iteration algorithm to determine crystal field parameters. Then, the magnetic-pole transition line strengths of Yb³⁺:Ba₂YB'O₆(B'=Ta⁵⁺, Nb⁵⁺) from (²F_5/2)Γ₈^- to the low-energy states were calculated.