发光材料BaAl2Si2O8∶Eu2+的物相结构与发光性能

A phosphor, Ba_0.97Al₂Si₂O₈∶Eu²⁺, was synthesized by high temperature solid-phase method at different temperatures. The samples were characterized by TG/DTA, XRD and fluorescence spectroscopy. The results show that the main phase for host of these luminescence materials is barium feldspar BaAl₂Si₂O₈∶Eu²⁺ and there is a transition from hexagonal crystal system to monoclinic crystal system in the process of the sintering of barium feldspar. The luminescent phenomen of barium feldspar with hexagonal structure can not be observed under the excitation of ultraviolet lamp of 365 nm while the barium feldspar with monoclinic structure has excellent luminescence properties. The excitation spectra of all these samples show broad band spectra ranging from 250～390 nm with peak at λ_ex of 357 nm，which indicates that these samples can be effectively excited by near ultraviolet ; the emission spectra range from 380～600 nm with peak at λ_em of 433 nm. The luminescent intensity increases then decreases with the concentration of doping Eu²⁺ ions. When the concentration of dopants is 2.5mol%, the luminescent intensity reaches the maximum value. When the concentration of Eu²⁺ ions changes from 0.5mol% to 2.5mol%, the emission peak has a red shift from 427 nm to 440 nm.

Phase Structure and Luminescence Properties of BaAl2Si2O8:Eu2+ Phosphor