Solubility and transport of water vapor in some 6FDA-based polyimides

Permeability, diffusion, and solubility coefficients for H₂O vapor in four different 6FDA-based polyimides were determined at temperatures between 25 and 45°C and over a wide range of relative humidities. The solubility of H₂O vapor in some of the polyimides studied can be described by the “dual-mode sorption” model whereas in other polyimides it is represented by the Flory-Huggins equation, which suggests that the latter polymers are plasticized by H₂O. The solubility of H₂O vapor in the polyimides decreases as the temperature is raised and increases with increasing polarity of the polymer. The diffusion coefficients for H₂O in the polyimides studied either increase or pass through a weak maximum with increasing H₂O activity, or concentration in the polymers. The latter behavior is probably due to a clustering of H₂O molecules in the polyimides at higher H₂O activities or concentrations. The diffusion coefficients for H₂O decrease as the chain-packing density of the polyimides increases. The permeability coefficients for H₂O vapor in 6FDA-based polyimide membranes either increase slightly or are constant as the H₂O activity is increased. The experimental values of the permeability coefficients are consistent with the values determined from diffusion and solubility coefficients. The permeability of the polyimides to H₂O vapor appears to be controlled by the solubility of H₂O in the polymers. The polyimides studied exhibit a very high selectivity for H₂O vapor relative to CH_4, and therefore are potentially useful membrane materials for the dehydration of natural gas. ©1995 John Wiley & Sons, Inc.