Exchange bias in bulk Ni-Mn-In-based Heusler alloys

The crystal structure and exchange bias of the bulk Heusler alloys Ni₅₀Mn_50−xIn_x with 14.5?x?15.2 have been investigated using X-ray diffraction and magnetization measurements, respectively. Magnetic measurements were performed with SQUID magnetometry after samples were zero-field cooled and field cooled (FC) in positive magnetic fields up to H=50 kOe, from a temperature T=380 K. Three temperatures of the phase transitions, T₁<T_M<T_C, and a shift of the FC (50 kOe) magnetic hysteresis loops up to 120 Oe at 5 K have been detected for all samples. The exchange bias field (H_E) was almost constant for intermediate In concentrations 14.8<x<15.2, and sharply decreased to about 20 Oe on the borders of this concentration interval (x?14.5; 15.2?x). The changes of H_E have been related to changes in the ratio of T₁ to T_M: the overlapping of transitions at T₁ and T_M (for x=14.8, and 15.2) results in a decrease in H_E.