Simultaneous variations of microstructure and magnetic properties of Ni58Fe12Zr20B10 nanostructure/amorphous alloy prepared by mechanical alloying

This study aims to evaluate magnetic and micro-structural properties of amorphous/nanocrystalline mechanically alloyed Ni₅₈Fe₁₂Zr₂₀B₁₀ powders with ball-milling time up to 190 h. Structural, micro-structural and thermal evaluations of the milled powders were carried out by X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM) and differential scanning calorimetry (DSC) methods. Magnetic properties were also measured by a vibrating sample magnetometer (VSM) instrument. Results showed that the amorphous phase reached maximum value of 95% and the crystallite size was about 3 nm at the end of the milling. Magnetization saturation (M_s) decreased slightly and coercivity (H_c) reached to the highest value at 72 h of the milling time. At the 190 h of milling, the coercivity and saturation magnetization reached 18 Oe and 20 emu/g, respectively. While, after an appropriate amount of heat treatment, these two variables became approximately 2 Oe and 32 emu/g.