Conductivity and dielectric properties of sol–gel derived porous zirconia

The 8-mol percentage Y₂O₃-stabilized Porous Zirconia was prepared using sol–gel method. Zirconium oxalate gel was prepared by the addition of appropriate amount of oxalic acid solution into the 1 M aqueous solution of zirconium-oxy chloride. A cubic phase zirconia powder was obtained by calcination and milling of the zirconium oxalate gel. Crystallization temperature was found about 450 °C from the Differential thermal analysis. The phase analysis by X-ray diffraction shows the presence of cubic phase. Pellets sintered at 1,350 °C were highly porous, and the electrical conductivity was found with lower value due to the porosity, and the hardness was about 8.0 GPa. Paper presented at the Third International Conference on Ionic Devices (ICID 2006), Chennai, Tamilnadu, India, Dec. 7–9, 2006.