In situ Investigations of Interfacial Degradation and Ion Migration at CH3NH3PbI3 Perovskite/Ag Interfaces

Interfacial properties between perovskite layers and metal electrodes play a crucial role in the device performance and the long-term stability of perovskite solar cells. Here, we report a comprehensive study of the interfacial degradation and ion migration at the interface between CH₃NH₃PbI₃ perovskite layer and Ag electrode. Using in situ photoemission spectroscopy measurements, we found that the Ag electrode could induce the degradation of perovskite layers, leading to the formation of PbI₂ and AgI species and the reduction of Pb²⁺ ions to metallic Pb species at the interface. The unconventional enhancement of the intensities of I 3d spectra provides direct experimental evidences for the migration of iodide ions from CH₃NH₃PbI₃ subsurface to Ag electrode. Moreover, the contact of Ag electrode and perovskite layers induces an interfacial dipole of 0.3 eV at CH₃NH₃PbI₃/Ag interfaces, which may further facilitate iodide ion di usion, resulting in the decomposition of perovskite layers and the corrosion of Ag electrode.