Preparation and characterisation of compositionally graded BaxSr1-xTiO3 thin films

Ba_xSr_1-xTiO₃ thin films with a compositional gradient of x=0.3 to 1 (in 0.1 mole fraction increments) were fabricated on Pt/Ti/SiO₂/Si substrates using a modified sol–gel technique. The graded film crystallised in a perovskite structure and consists of a uniform microstructure with comparatively larger grains. The room-temperature relative dielectric constant (ε_r) and dielectric loss (cosδ) at 100 kHz were found to be 305 and 0.03 respectively. Dielectric peaks were not observed in the temperature range from -20 °C to 120 °C. The dielectric constant and dielectric loss were almost independent of temperature. Polarisation–electric field measurements at room temperature revealed a saturated but slim hysteresis loop with a remanent polarisation (P_r) of 0.6 μC/cm² and a coercive field (E_c) of 2.4 kV/mm. The graded film behaves as a stack of Ba_xSr_1-xTiO₃ capacitors connected in series and hence the dielectric Curie peaks are removed. Received: 4 October 2001 / Accepted: 17 October 2001 / Published online: 23 January 2002