| Anomalous magnetic properties of an iron film system deposited on fracture surfaces of α-Al2O3 ceramics |
| |
| 引用本文： | 焦志伟,陈苗根,姜伟棣,冯春木,叶高翔. Anomalous magnetic properties of an iron film system deposited on fracture surfaces of α-Al2O3 ceramics[J]. 中国物理 B, 2008, 17(9): 3499-3504 |
| |
| 作者姓名： | 焦志伟 陈苗根 姜伟棣 冯春木 叶高翔 |
| |
| 作者单位： | Department of Physics, Zhejiang University,Hangzhou310027, China;Department of Physics, China Jiliang University, Hangzhou 310018, China;Department of Physics, China Jiliang University, Hangzhou 310018, China;Department of Physics, China Jiliang University, Hangzhou 310018, China;Test and Analysis Center, Zhejiang University, Hangzhou310028, China;Department of Physics, Zhejiang University,Hangzhou310027, China |
| |
| 基金项目： | Project supported by the NationalNatural Science Foundation of China (Grant Nos 10574109 and50701037) and the Zhejiang Provincial Scienceand Technology Department of China (Grant No 2005C24008). |
| |
| 摘 要： | An iron film percolation system is fabricated by vapour-phase deposition on fracture surfaces of α-Al2O3 ceramics. The zero-field-cooled （ZFC） and field-cooled （FC） magnetization measurement reveals that the magnetic phase of the film samples evolve from a high-temperature ferromagnetic state to a low-temperature spin-glass-like state, which is also demonstrated by the temperature-dependent ac susceptibility of the iron films. The temperature dependence of the exchange bias field He of the iron film exhibits a minimum peak around the temperature T=5 K, which is independent of the magnitude of the cooling field Hcf. However, for T 〉 10K, （1） He is always negative when Hcf=2kOe and （2） for Hcf= 20 kOe （1Oe≈80 A/m）, He changes from negative to positive values as T increases. Our experimental results show that the anomalous hysteresis properties mainly result from the oxide surfaces of the films with spin-glass-like phase.
|
| 关 键 词： | 交换相互作用 磁测量 铁膜 制陶术 |
| 收稿时间： | 2007-11-07 |
Anomalous magnetic properties of an iron film system deposited on fracture surfaces of α-Al2O3 ceramics |
| |
| Jiao Zhi-Wei,Chen Miao-Gen,Jiang Wei-Di,Feng Chun-Mu and Ye Gao-Xiang. Anomalous magnetic properties of an iron film system deposited on fracture surfaces of α-Al2O3 ceramics[J]. Chinese Physics B, 2008, 17(9): 3499-3504 |
| |
| Authors: | Jiao Zhi-Wei Chen Miao-Gen Jiang Wei-Di Feng Chun-Mu Ye Gao-Xiang |
| |
| Affiliation: | Department of Physics, China Jiliang University, Hangzhou 310018, China; Department of Physics, Zhejiang University,Hangzhou310027, China; Department of Physics, Zhejiang University,Hangzhou310027, China;Department of Physics, China Jiliang University, Hangzhou 310018, China; Test and Analysis Center, Zhejiang University, Hangzhou310028, China |
| |
| Abstract: | An iron film percolation system is fabricated by vapour-phasedeposition on fracture surfaces of α-Al2O3 ceramics.The zero-field-cooled (ZFC) and field-cooled (FC) magnetizationmeasurement reveals that the magnetic phase of the film samplesevolve from a high-temperature ferromagnetic state to alow-temperature spin-glass-like state, which is also demonstrated bythe temperature-dependent ac susceptibility of the iron films. Thetemperature dependence of the exchange bias field $H_{rm e}$ of theiron film exhibits a minimum peak around the temperature $T$=5,K,which is independent of the magnitude of the cooling field $H_{rmcf}$. However, for $T > 10$,K, (1) $H_{rm e}$ is always negativewhen $H_{rm cf}$=2,kOe and (2) for $H_{rm cf }$= 20,kOe(1Oe$approx$80,A/m), $H_{rm e}$ changes from negative to positivevalues as T increases. Our experimental results show that theanomalous hysteresis properties mainly result from the oxidesurfaces of the films with spin-glass-like phase. |
| |
| Keywords: | iron film ceramics exchangeinteractions magnetic measurements |