Synthesis and Characterization of a Fluorescent Water-Borne Polyurethane Based on a Novel Naphthalimide Dye

A waterborne-polyurethane (WPU) dye, based on the fluorescent dye 4-diamino propane-N-allyl-1,8- naphthalimide (WPU-DAN), was synthesized by attaching 4-diamino propane-N-allyl-1,8- naphthalimide (DAN) onto both ends of the polyurethane (PU) chains according to a prepolymer?ionomer process. The synthetic process was confirmed by Fourier transform infrared spectroscopy (FTIR) and UV-visible absorption. The glass transition temperature, molecular weight and average particle sizes were measured. The glass transition temperatures of WPU and WPU-DAN were 46.6 and 49.8°C, respectively. In addition, the particle size distributions of WPU-DAN and WPU were 140 and 134 nm, respectively. The thermal behaviour of WPU-DAN showed improvement compared to WPU. The fluorescence intensity of WPU-DAN was enhanced more than DAN due to the naphthalimide groups attached to the chains, and the fluorescence intensity of WPU-DAN and DAN were increased by increasing temperature. Moreover, the fluorescence intensity of WPU-DAN emulsion was stable during 30 days and no loss of fluorescence intensity occurred for these days.