Si nanocrystallites in SiO2 with intense visible photoluminescence synthesized from SiOx films deposited by laser ablation

We observed very intense and highly reproducible photoluminescence (PL) spectra for SiO_x films obtained by laser ablation of Si targets in 50-mTorr oxygen gas followed by proper annealing. It was found that the PL peak continuously changes from 1.4 eV at the center of the samples to 1.8 eV at the sample edge. The optimum values of the oxygen component in SiO_x was x=1.3-1.4 and the optimum annealing temperature was 1000 °C for intense PL. From transmission electron microscopy images of annealed films, Si nanocrystallites are found to be formed in the matrix of SiO₂ grown from the SiO_x and have diameters of 2-3 nm. These indicate that a high density of Si nanocrystallites with diameters of 2-3 nm in the SiO₂ phase are probably responsible for the PL and that the Si nanostructure is well formed from the as-deposited, metastable SiO_x (x=1.3-1.4) films by annealing at 1000 °C.