Crystallization and dielectric properties of low temperature dielectrics containing Li2O filler

Crystallization and dielectric properties of typical low temperature co-fired ceramics (LTCC) consisting of calcium zinc aluminoborosilicate glass and Al₂O₃ filler were investigated by substituting the Al₂O₃ filler partially with Li₂O at the levels of 2-10 wt%. Depending on the content of Li₂O, densification was found significantly affected by early crystallization that resulted from the formation of unexpected crystalline phases including LiAlSiO₄, Ca₂SiO₄, LiAlO₂, and LiAlSi₃O₈. The effect of hindering sintering via earlier crystallization became enormous regardless of firing temperature when >5 wt% Li₂O substitution occurred. It was observed that the substitution of 2 wt% Li₂O for Al₂O₃ was beneficial in producing promising performance at the low temperature of 750 °C, which can be highlighted with k ∼ 8.7 and tan δ ∼ 0.009 at 1 MHz.