Effective electro‐optic coefficient of (1–x)Pb(Zn1/3Nb2/3)O3–xPbTiO3 single crystals

Refractive indices and effective electro‐optic coefficient γ_c of (1–x)Pb(Zn_1/3Nb_2/3)O₃–xPbTiO₃ (PZN‐xPT, x = 0.05, 0.09 and 0.12) single crystals were measured at 532 nm wavelength. Orientation and temperature dependences of the electro‐optic coefficient were investigated. Large electro‐optic coefficient (γ_c = 470 pm/V) was observed in 001]‐poled PZN‐0.09PT crystal. More importantly, γ_c of tetragonal PZN‐0.12PT is almost unchanged in a temperature range ?20 ～ 80 °C. The γ_c of PZN‐xPT single crystals are much higher than that of widely used electro‐optic crystal LiNbO₃ (γ_c = 20 pm/V). These results show that PZN‐xPT single crystals are very promising materials for electro‐optic modulators in optical communications.