Thermodynamic properties of iron—selenium alloys |
| |
Authors: | Wilfried Schuster Herbert Ipser Kurt L. Komarek |
| |
Affiliation: | (1) Institute of Inorganic Chemistry, University of Vienna, A-1090 Vienna, Austria |
| |
Abstract: | Selenium vapor pressures of iron-selenium alloys were determined by an isopiestic method between 700 and 1 200 K and 50 to 60 at%Se, and activities and partial molar enthalpies of selenium were calculated. ByGibbs-Duhem integration activities of iron, and integralGibbs energies were obtained. A theoretical model was successfully applied to interprete the thermodynamic properties of the hexagonal -phase with NiAs-structure. Assuming a random distribution of iron vacancies in every transition metal layer of the lattice excellent agreement with experimental data was found. The energy of interaction betwen iron vacancies was calculated to be 147.0 kJ/g-atom.
Thermodynamische Eigenschaften von Eisen—Selen—Legierungen Zusammenfassung Die Selendampfdrücke von Eisen-Selen-Legierungen wurden mit Hilfe einer isopiestischen Methode zwischen 700 und 1 200 K und zwischen 50 und 60 At%Se bestimmt. Daraus wurden die Aktivitäten und die partiellen molaren Enthalpien von Selen berechnet, und über eineGibbs-Duhem-Integration wurden die Eisen-Aktivitäten und die integralenGibbs'schen Energien erhalten. Ein theoretisches Modell wurde erfolgreich angewendet, um die thermodynamischen Eigenschaften in der hexagonalen NiAs-Phase zu interpretieren. Unter der Annahme einer statistischen Verteilung von Eisen-Leerstellen über sämtliche Übergangsmetall-Schichten wurde eine ausgezeichnete Übereinstimmung mit den experimentell gefundenen Daten festgestellt. Die Wechsel-wirkungsenergie zwischen diesen Leerstellen wurde zu 147,0 kJ/g-atom ermittelt. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|