Glass formation in the MoO3–Nd2O3–La2O3–B2O3 system

In MoO₃–Nd₂O₃–B₂O₃ and MoO₃–Nd₂O₃–La₂O₃–B₂O₃ systems, glasses were obtained in the region between 20 and 30 mol% Ln₂O₃. A liquid-phase separation region was observed near the MoO₃–B₂O₃ side up to 20 mol% Ln₂O₃ (La, Nd). The amorphous phases were characterized by X-ray diffraction (XRD), differential thermal analysis (DTA), UV–VIS and infrared spectroscopy (IR). According to DTA data B₂O₃-rich glasses are stable up to 630 °C while glasses rich in MoO₃ are stable up to 430 °C. The glasses are transparent in the visible region. Structural models for the glasses network were suggested on the basis of IR spectral investigations. It was established that BO₃ (1380 cm⁻¹), BO₄ (1100–950 cm⁻¹) and MoO₄ (860 cm⁻¹) groups build up the glass network. MoO₆ units (band at 880 cm⁻¹) together with BO₃ units participate in the formation of the glass network with a high MoO₃ content (80–90 mol%).