Solution Blowing of Poly(dimethylsiloxane)/Nylon 6 Nanofiber Mats for Protective Applications
引用本文:程博闻.Solution Blowing of Poly(dimethylsiloxane)/Nylon 6 Nanofiber Mats for Protective Applications[J].高分子科学,2014,32(6):786-792.
作者姓名:程博闻
作者单位:[1]School of Textiles, Tianjin Polytechnic University, Tianjin 300387, China [2]Key Laboratory of Advanced Textile Composite Materials of Ministry of Education, Tianjin Polytechnic University, Tianjin 300387, China
基金项目:This work was financially supported by the National Natural Science Foundation of China (Nos. 51103104 and 51173131), Tianjin Natural Science Foundation (13JCZDJC32600).
摘    要:A new strategy was developed to fabricate superhydrophobic nylon 6 nanofibers, in which the blend solutions of poly(dimethylsiloxane)(PDMS) prepolymer and nylon 6 was spun using an innovative solution blowing process, and then the PDMS prepolymer contianning nanofibers were cured to obtain PDMS/nylon 6 nanofiber mats. Morphology, surface composition, non-wetting property and protective performance were investigated. The results showed that the addition of PDMS prepolymer improved the spinnability of the spinning solutions, and the PDMS/nylon 6 nanofibers had smooth surfaces and diameters from 100 nm to 350 nm. The presence of PDMS effectively enhanced the hydrophobicity of the nanofiber mats, showing water contact angles of 132° to 161° for PDMS contents of 1 wt% to 3 wt%. The PDMS/nylon 6 mats also possessed excellent protective and transport properties. The results indicated the potential application of the novel nanofiber mats in protective clothing.

关 键 词:聚二甲基硅氧烷  纳米纤维膜  尼龙6  保护性  应用  PDMS  纺丝溶液  超疏水性

Solution blowing of poly(dimethylsiloxane)/nylon 6 nanofiber mats for protective applications
Lei Shi,Xu-pin Zhuang,Bo-wen Cheng,Xiao-xiao Tao,Wei-min Kang.Solution blowing of poly(dimethylsiloxane)/nylon 6 nanofiber mats for protective applications[J].Chinese Journal of Polymer Science,2014,32(6):786-792.
Authors:Lei Shi  Xu-pin Zhuang  Bo-wen Cheng  Xiao-xiao Tao  Wei-min Kang
Institution:1. School of Textiles, Tianjin Polytechnic University, Tianjin, 300387, China
2. Key Laboratory of Advanced Textile Composite Materials of Ministry of Education, Tianjin Polytechnic University, Tianjin, 300387, China
Abstract:A new strategy was developed to fabricate superhydrophobic nylon 6 nanofibers, in which the blend solutions of poly(dimethylsiloxane) (PDMS) prepolymer and nylon 6 was spun using an innovative solution blowing process, and then the PDMS prepolymer contianning nanofibers were cured to obtain PDMS/nylon 6 nanofiber mats. Morphology, surface composition, non-wetting property and protective performance were investigated. The results showed that the addition of PDMS prepolymer improved the spinnability of the spinning solutions, and the PDMS/nylon 6 nanofibers had smooth surfaces and diameters from 100 nm to 350 nm. The presence of PDMS effectively enhanced the hydrophobicity of the nanofiber mats, showing water contact angles of 132° to 161° for PDMS contents of 1 wt% to 3 wt%. The PDMS/nylon 6 mats also possessed excellent protective and transport properties. The results indicated the potential application of the novel nanofiber mats in protective clothing.
Keywords:Nanofiber  Solution blowing  Hydrophobicity  Protective clothing  PDMS  