The structural evolution of alkoxy-derived gel during drying
Authors:Atsuo Yasumori  Hiroshi Kawazoe and Masayuki Yamane
Institution:

Department of Inorganic Materials, Tokyo Institute of Technology, 2-12-1 Ookayama, Meguro-ku, Tokyo 152, Japan

Abstract:The effects of drying temperature on the structural evolution of alkoxy-derived silica gel prepared using various catalysts have been investigated. The dependence of specific surface area, Sg, reflecting the structure, on the temperature of drying was remarkable for a non-catalyzed xerogel. The effect of drying temperature on the Sg of an ammonia-catalyzed xerogel was also found but was not very large. The Sg of xerogels obtained by drying at 60°C was always higher by 50% than the gels dried at 30°C without regard to the aging temperature. The Sg of xerogels from HCl-catalyzed solution was of the order of several m2/g, however, the Sg of the aerogel obtained by hypercritical drying of the wet gel from a similar solution was about 800 m2/g. These phenomena were understood on the basis of SAXS measurements on both wet gels and aerogels.
Keywords:
本文献已被 ScienceDirect 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号