(英)退火温度对电子束蒸发沉积硅薄膜结构和光学性能的影响
引用本文:刘保剑,段微波,李大琪,余德明,陈刚,刘定权. (英)退火温度对电子束蒸发沉积硅薄膜结构和光学性能的影响[J]. 红外与毫米波学报, 2020, 39(1): 1-5. DOI: 10.11972/j.issn.1001-9014.2020.01.001
作者姓名:刘保剑  段微波  李大琪  余德明  陈刚  刘定权
作者单位:中国科学院上海技术物理研究所,上海 200083;中国科学院上海技术物理研究所,上海 200083;中国科学院上海技术物理研究所,上海 200083;中国科学院上海技术物理研究所,上海 200083;中国科学院上海技术物理研究所,上海 200083;中国科学院上海技术物理研究所,上海 200083
基金项目:the National Natural Science Foundation of China 61605229;Innovation Program of Shanghai Institute of Technical Physics, Chinese Academy of Sciences CX-129Supported by the National Natural Science Foundation of China (61605229); Innovation Program of Shanghai Institute of Technical Physics, Chinese Academy of Sciences (CX-129)
摘    要:系统研究了退火温度对硅薄膜结构和光学性能的影响。通过电子束蒸发工艺制备硅薄膜,然后在氮气保护下对薄膜样品在200~500°C范围内进行退火处理。使用XRD、拉曼光谱、电子自旋共振和透射光谱测量等方法对薄膜样品进行了表征。结果显示,随着退火温度的升高,非晶硅薄膜结构有序度在短程和中程范围内得到改善,同时缺陷密度显著降低-。当样品在400°C退火后,消光系数k由6.14×10-3下降到最小值1.02×10~3(1000 nm),这是由于此时硅薄膜缺陷密度也降到最低,约为沉积态薄膜的五分之一。试验结果表明,硅薄膜在适当的温度下退火可以有效地降低近红外区膜层的光学吸收,这对硅薄膜在光学薄膜器件研制中具有重要应用。

关 键 词:光学薄膜  硅薄膜  光学性能  退火
收稿时间:2019-04-17
修稿时间:2019-12-17

The influence of annealing temperature on the structure and optical properties of silicon films deposited by electron beam evaporation
LIU Bao-Jian,DUAN Wei-Bo,LI Da-Qi,YU De-Ming,CHEN Gang and LIU Ding-Quan. The influence of annealing temperature on the structure and optical properties of silicon films deposited by electron beam evaporation[J]. Journal of Infrared and Millimeter Waves, 2020, 39(1): 1-5. DOI: 10.11972/j.issn.1001-9014.2020.01.001
Authors:LIU Bao-Jian  DUAN Wei-Bo  LI Da-Qi  YU De-Ming  CHEN Gang  LIU Ding-Quan
Affiliation:Shanghai Institute of Technical Physics, Chinese Academy of Sciences, Shanghai 200083, China,Shanghai Institute of Technical Physics, Chinese Academy of Sciences, Shanghai 200083, China,Shanghai Institute of Technical Physics, Chinese Academy of Sciences, Shanghai 200083, China,Shanghai Institute of Technical Physics, Chinese Academy of Sciences, Shanghai 200083, China,Shanghai Institute of Technical Physics, Chinese Academy of Sciences, Shanghai 200083, China,Shanghai Institute of Technical Physics, Chinese Academy of Sciences, Shanghai 200083, China
Abstract:In this paper,the influence of annealing temperature on the structure and optical properties of silicon films was systemically investigated.Silicon films were deposited by electron beam evaporation and then annealed in N2 atmosphere within a temperature range from 200 to 500°C.The films were characterized by X-ray diffraction(XRD),Raman spectroscopy,electronicspin resonance(ESR)and optical transmittance measurement,respectively.With annealing temperature increased,the amorphous network order of silicon films was improved on the short and medium range and the defect density decreased remarkably.When sample being annealed at 400°C,the extinction coefficient k decreased from 6.14×10-3 to a minimum value of 1.02×10-3(at 1000 nm),which was due to the lowest defect density,about one fifth of the as-deposited sample.The results showed that annealing at an appropriate temperature could effectively reduce the optical absorption of silicon films in the near infrared region,which were very critical for the application in optical thin film coating devices.
Keywords:optical coatings  silicon films  optical properties  annealing