Pulsed NMR observation of ultradrawn polypropylene

Proton spin-spin relaxation times have been measured as a function of temperature for ultradrawn polypropylene with draw ratios λ up to 24. The three relaxation times T_2a (the longest), T_2i (intermediate), and T_2c (the shortest), observed for all the samples, have been ascribed to the relaxations of the amorphous, constrained amorphous, and crystalline components, respectively. T_2i and T_2a, which reflect the changes in structure and mobility in the noncrystalline regions, decrease with increasing λ; T_2i becomes saturated at λ > 9, whereas T_2a shows a substantial decrease up to λ = 24. The continued decrease in T_2a indicates that the constraint on the amorphous segments keeps increasing up to the highest λ. The associated mass fractions F_a, F_i, and F_c also change with λ. At λ < 9, the increasc in F_i with increasing λ is accompanied by a decrease in F_a, with F_c remaining unchanged. At higher λ, however, F_a is almost constant, and stepwise rises in F_c at about λ = 12 and 24 are accompanied by corresponding drops in F_i. It seems that, in this high draw ratio range, some of the taut molecules are fully extended and are in sufficiently good lateral register to transform into crystalline bridges. This conjecture is supported by the similarity in the λ dependence of F_c and the mass-fraction crystallinity obtained from the heat of fusion.