CRYSTAL STRUCTURE AND MORPHOLOGY OF NASCENT SAMPLES OF SYMMETRIC AROMATIC POLYESTERS——Ⅱ. POLY(p-PHENYLENE 2,6-NAPHTHALATE) |
| |
作者姓名: | G.Sidoti F.Rybnikar M.Kaszonyiova P.H.Geil |
| |
作者单位: | Department of Materials Science and Engineering University of Illinois,Urbana,IL 61801,Department of Materials Science and Engineering,University of Illinois,Urbana,IL 61801 Tomas Bata University of Zlin,Zlin,Czech Republic,Tomas Bata University of Zlin,Zlin,Czech Republic,Department of Materials Science and Engineering,University of Illinois,Urbana,IL 61801 |
| |
基金项目: | This research was supported, in part, by grants from the National Science Foundation (NSF-DMR International Program 96-16255 (F. R. and P. H. G.) and NSF-DMR Polymer Program 93-12823 and 96-16255 (J. Y., G. S., J. L. and P. H. G.) and Grant Agency of the |
| |
摘 要: | Confined thin film melt polymerization (CTFMP) of naphthalene chloride/hydroquinone (NCMQ, 1/1, molar)mixtures at polymerization temperatures (T_p) below ca. 300℃ resulted in relatively thick, elongated crystals. Polymerizationof NC/HQ above 300℃ between glass yielded well-formed lamellar crystals ca. 100 A thick. Phase Ⅰ and Ⅱ [001] EDpatterns were obtained for all T_p, the relative amount of phase Ⅰ increasing with T_p. Polymerization of naphthalenedicarboxylic acid/hydroquinione diacetate 1/1 mixtures at high T_p also yielded lamellar crystals that "curled up" off of thesubstrate. When the high temperature CTFMP polymerization was conducted between mica, aggregates of lamellae on-edgedeveloped but epitaxial growth did not occur. Epitaxial growth of lamellae between mica could be obtained, however, byconfined thin film solution polymerization, with both of the latter samples yielding apparently related ED patterns from adifferent unit cell than phase Ⅰ or Ⅱ. Fiber patterns, obtained from sheared samples, indicated considerably greater crystaldisorder than in the nascent crystals. Refinement of the phase Ⅰ unit cell parameters, based on the [001] and [01 1] EDpatterns, with modeling based on Cerius~2, suggests a monoclinic phase Ⅰ unit cell with a = 7.76, b = 5.71, c = 14.99 A, α = γ= 90°, β= 99.7°, ρ = 1.47 g/cm~3, space group P12_1/al.
|
本文献已被 CNKI 等数据库收录! |
|