Effect of Corrosion in Alkaline Solution to the Microstructure and Mechanical Properties of Cu/Sn-9Zn/Cu |
| |
Institution: | 1. School of Materials and Mineral Resources Engineering, Universiti Sains Malaysia, 14300, Nibong Tebal, Penang, Malaysia;2. Center of Excellence Geopolymer & Green Technology (CEGeoGTech), School of Materials Engineering, Universiti Malaysia Perlis, 02600 Jejawi, Perlis, Malaysia |
| |
Abstract: | Corrosion resistance performance of binary eutectic tin-zinc (Sn-9Zn) solder was investigated in 6 M potassium hydroxide. The corrosion resistance performance of the solder was studied through potentiodynamic polarization. Double dissolution peaks were seen during polarization, indicating preferential dissolution of elements from this solder. Tensile strength measurement shows substantial loss of ultimate tensile strength (UTS) of the joint made after polarization. Microstructure characterization proved that weak spots were introduced as active elements removed during polarization. This showed that microstructure alteration contributed to the loss of UTS after polarization. |
| |
Keywords: | Lead-free solder Sn-9Zn Corrosion Joint Alkaline |
本文献已被 ScienceDirect 等数据库收录! |
|