Further investigations on the temperature-dependence of magnetic susceptibility and thermogravimetry of stoichiometric antimony triselenide and antimony tritelluride semiconductors |
| |
| Authors: | M M Abou-Sekkina |
| |
| Institution: | (1) Faculty of Science, Tanta University, Tanta, Egypt;(2) Present address: Faculty of Science, The United Arab Emirates University, P.O. Box 15551, Al-Ain, UAE |
| |
| Abstract: | Stoichiometrically adjusted antimony triselenide and antimony tritelluride semiconductors were carefully prepared for the first time. Numerous measurements were carried out, involving X-ray diffraction analysis, true density, thermogravimetric analysis and the temperature-dependence of the magnetic susceptibility. The results obtained indicated that antimony triselenide and antimony tritelluride polycrystals possess mass susceptibilities of –0.361×10–6 and –0.386×10–6 C.G.S., respectively. The results are discussed on the basis of electronegativity difference, partial ionicity of the bond, and bond strength.
Zusammenfassung Stöchiometrische Antimontriselenid- und Antimontritellurid-Halbleiter wurden erstmals hergestellt. Zahlreiche Messungen wurden daran ausgeführt, und zwar Röntgendiffraktometrie, wahre Dichte, Thermogravimetrie und Temperaturabhängigkeit der magnetischen Susceptibilität. Die erhaltenen Ergebnisse zeigen, daß Polykristalle von Antimontriselenid und Antimontritellurid Massensusceptibilitäten von –0.361 · 10–6 bzw. –0.386 ·10–6 c.g.s. besitzen. Die erhaltenen Ergebnisse werden auf der Basis der Elektronegativitätsdifferenz, der partiellen Ionisierung und der Bindungsstärken diskutiert.
                    -     .  , ,  . ,   - , , –0,361 · 10–6 -0,386 · 10–6   .   , .
|
| |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ |
|