Crystallization of 2(Ca,Sr,Ba)O-TiO2-2SiO2 composition glasses

Crystallization was examined for glasses having chemical composition of 2(Ca,Sr,Ba)O-TiO₂-2SiO₂ in which the CaO/SrO/BaO molar ratio varied. Powdered glass samples were pelleted into disks and sintered at 950 °C for 2 h. The major phase precipitated in the sintered samples was (Ca,Sr,Ba)₂TiSi₂O₈ and minor phase of perovskite such as CaTiO₃ or SrTiO₃ increased with CaO content in the samples containing more than 40 mol% of CaO in total CaO+SrO+BaO. Three regions having different slopes were found in linear relationships between SrO mol% and exothermal peak temperature on DSC curves or d0 0 2] values determined by powder XRD method. These facts suggested that the major phase precipitated in each region was a solid solution containing a different amount of CaO, SrO, BaO and that these compositions varied depending on SrO content in the sample. The micro-crystalline structure, which could be useful in fabricating a dielectric dense body, was observed for samples containing 30-70 mol% of SrO.