Preparation of a novel Ni/Co-based alloy gradient coating on surface of the crystallizer copper alloy by laser |
| |
Authors: | Suiyuan Chen Jing LiangChangsheng Liu Kai SunJyoti Mazumder |
| |
Institution: | a Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education) Northeastern University, Shenyang 110004, China b Department of Materials Science and Engineering, University of Michigan, Ann Arbor, MI 48109, USA |
| |
Abstract: | A high wear-resistant gradient coating made of Ni/Co-based alloys on the surface of a Cu alloy substrate was synthesized using a YAG laser induced in situ reaction method. The coating consists of three layers: the first is a Ni-based alloy layer, the second and third are Co-based alloy layers. The microhardness increases gradually from 98 HV in the Cu alloy substrate to the highest level of 876 HV in the third layer. The main phase of the Co-based alloy layer is CoCr2(Ni,O)4, coexisting with the Fe13Mo2B5, Cr(Co(Mo, and FeCr0.29Ni0.16C0.06 phases. Wear tests indicate that the gradient coating has good bond strength and wear properties with a wear coefficient of 0.31 (0.50 for the Cu alloy substrate). Also, the wear loss of the coating is only 0.01 g after it has been abraded for 60 min, which is only one fifth of that of the Cu alloy of the crystallizer. Wear tests of the gradient coating reveal good adhesive friction and wear properties when sliding against steel under dry conditions. This novel technique may have good application to make an advanced coating on the surface of the Cu alloy crystallizer in a continuous casting process. |
| |
Keywords: | Gradient coating Laser cladding Hard particle phase Hardness Wear properties |
本文献已被 ScienceDirect 等数据库收录! |
|