Dispersion state of CuO on CeO2

XRD and XPS are used to study the dispersion state of CuO on ceria surface. The dispersion capacity values of CuO measured by the two methods are consistent, which are of 1.20 mmol CuO/100 m² CeO₂. In addition, the results reveal that highly dispersed Cu²⁺ ions are formed at low CuO loadings and that increasing the CuO content to a value higher than its dispersion capacity produces crystalline CuO after the surface vacant sites on CeO₂ are filled. The atomic composition of the outermost layer of the CuO/CeO₂ samples has been probed by using static secondary ion mass spectroscopy (SSIMS), and the ratim of Cu/Ce are found to be 0.93 and 0.46 for the 1.22 and 0.61 mmol CuO/CeO₂ samples respectively. Temperature-programmed reduction (TPR) profile with two reduction peaks at 156 and 165°C suggests that the reduction of highly dispersed Cu²⁺ ions consists of two steps and is easier than that of CuO crystallites, in which the TPR profile has only one reduction peak at about 249°C. The above experimental results are in good agreement with the prediction of the incorporation model. Project supported by the National Natural Science Foundation of China.