C.w. Laser annealing of amorphous Fe40Ni40P14B6: Effects on magnetostriction and young modulus

Summary C.w. laser annealing of metglas 2826 ribbons was performed by varying beam power and irradiation time. A simplified thermal model was elaborated to have information about the temperature rise of the samples and the occurrence of crystallization. The predictions were in agreement with the experimental results. The laser-induced changes of magnetic and mechanical properties were particularly tested by means of the magnetostrictive response and the Young-modulus variations.

---

Riassunto Sono stati trattati termicamente mediante irradiazione laser continua dei provini nastriformi di metglas 2826. Diverse condizioni sono state ottenute variando la potenza del fascio e la durata dell'irradiazione. Un semplice modello termico ha consentito di ottenere le temperature raggiunte nei vari trattamenti e di stimare la possibilità di realizare o meno la cristallizzazione. Le previsioni sono state ben verificate dai risultati sperimentali. In particolare si sono misurate variazioni della magnetostrizione e del modulo di Young coerenti anche con le indicazioni della precedente letteratura.

---

Резюме Проводится C.w.-лазерный отжиг 2826 узких полосок Fe₄₀Ni₄₀P₁₄B₆; изменяя мощность пучка и время облучения. Разработана упрощенная модель для получения информации об увеличении температуры образцов и появлении кристаллизаџии. Предсказания согласуются с экспериментальными результатами. Изменения магнитных и механических свойств, индуцированные лазером, частично проверяются с помощью изменений магнитострикционного отклика и модуля юнга.