| Abstract: | Calorimetric and dilatometric studies have been made of the fusion process of linear polyethylene crystals precipitated by high speed stirring from solution. It is shown that long-time annealing at elevated temperatures alleviates the superheating observed when rapid heating rates are employed. By the annealing procedures that have been adopted, a small but demonstrable fraction of high melting material can be produced whose melting temperature depends on the crystallization temperature. For crystallization at 105°C, followed by annealing at 142°C, a melting temperature of 146.0 ± 0.5°C is observed. The dissolution temperature in xylene, determined for the same sample, is consistent with the high melting temperature observed for the pure polymer. It is recognized that a state of high axial orientation need not necessarily be identified with extended chain crystals. Consequently, the increased melting temperature can result from either an increase in the crystallite size or a reduced interfacial free energy relative to crystallites produced by the more conventional mode of crystallization. |