Absorption spectra and magneto-optic figures of merit in the Bi x Sm3-x Fe5-y Ga y O12 system

The absorption (α) and Faraday rotation (θ) spectra of 14 garnets belonging to the series Bi _x Sm_3-x Fe_5-y Ga _y O₁₂ (0<x<1.05, 0.8<y<1.15) have been measured between 15 000 cm⁻¹ and 19 000 cm⁻¹. The figure of merit (θ/α) at 17 850 cm⁻¹ (560 nm) increases linearly with increasing bismuth concentration up tox∼0.6 where it begins to increase less rapidly. For operation of magneto-optic display devices at 17 850 cm⁻¹ there is no advantage in using garnets in this series withx>0.8. The Faraday rotation at 17 850 cm⁻¹ increases linearly with bismuth concentration whereas the absorption coefficient increases more rapidly. The presence of Bi³⁺ increases the intensity of all Fe³⁺ pair transitions in the garnet system as a result of the increased superexchange induced by Bi³⁺. This is in keeping with the observation that the intensity of the⁶A_1g (S)→⁴T_1g (G) transition in (RE)₃Fe₅O₁₂ (RE=Er, Y, Dy, Gd, Eu) increases on traversing the above RE series as do the Curie temperatures of these iron garnets.