Superconductivity in Ba2−xSrxYCu3Oz prepared at GPa

The compounds Ba_1.4Sr_0.6YCu₃O_z (7.0≤z<7.4) were synthesized at 2 GPa to clarify the effect of high temperature and pressure on the superconducting properties. The structure as observed by powder X-ray diffraction was tetragonal for z≥7.2, and orthorhombic or tetragonal for z<7.1. It has been revealed that high-pressure syntheses suppress the superconductivity in the compounds with z<7.1. Recovery of the superconducting properties occurs above z≥7.2. The effect of Sr substitution on the superconducting properties was also studied. The magnitude of diamagnetism at 5–30 K decreases monotonically from −0.003 to −0.0002 emu/g Oe with increasing x in Ba_2−xSr_xYCu₃O_z (x≥1.2).