Magnetic susceptibility of liquid gold-indium-zinc alloys

Summary Alloys of the ternary system gold-indium-zinc with a variable content of goldx _Au at a constant ratio ofx _In:x _Zn=1:1 have been investigated by susceptibility measurements from 300 K up to 1500 K with emphasis on the liquid state. The magnetic susceptibilities of the homogeneous liquids were found to vary in a non-linear manner with temperature and composition. At temperatures close to the liquid-solid transition, the susceptibilities pass through a characteristic minimum which tends to disappear with increasing temperature. The anomaly located atx _Au 0.6 seems to be related to a particular valence electron concentration ofe/a 1.6.

---

Magnetische Suszeptibilität von flüssigen Gold-Indium-Zink-Legierungen

Zusammenfassung Legierungen des ternären Systems Gold-Indium-Zink mit einem variablen Goldgehaltx _Au bei konstantem Indium-Zink-Verhältnis (x _In:x _Zn=1:1) wurden zwischen 300 und 1500 K auf ihre magnetische Suszeptibilität untersucht. Das Hauptaugenmerk wurde dabei auf den flüssigen Zustand gelegt. Die magnetischen Suszeptibilitäten der homogenen Schmelzen variieren nichtlinear mit Temperatur und Zusammensetzung. Bei Temperaturen nahe dem übergang flüssig-fest tritt ein charakteristisches Minimum der Suszeptibilität auf, das mit steigender Temperatur verschwindet. Die Anomalie bei einemx _Au vonca. 0.6 scheint mit einer speziellen Valenzelektronenkonzentration (e/a) von etwa 1.6 verknüpft zu sein.