Electrical properties of phosphate glasses

The electrical properties of glasses in the Na₂OP₂O₅, Ag₂OP₂O₅ and (1?x)Na₂OxAg₂OP₂O₅ systems have been measured over a range of temperature and composition.The properties of the Na₂OP₂O₅ and Ag₂OP₂O₅ glasses have been compared within the phosphate system as well as with silicate glasses. The silver-containing glasses show higher conductivity and lower temperature coefficients when compared with the sodium-containing glasses. A maximum in the room temperature resistivity of the (1?x)Na₂O?xAg₂O?P₂O₅ system was found around the mole ratio of 0.16:0.84 Ag₂O:Na₂O, indicating a mixed-alkali effect. A similar effect was seen in the tan δ, but not in the T_g-against-composition plots. A linear relationship was noted for the tan δ-versus-log₁₀ (resistivity) plot, as has been seen in other glass-forming systems.