Effect of heat treatment on particle growth and magnetic properties of electrospun Sr0.8La0.2Zn0.2Fe11.8O19 nanofibers

Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉/poly(vinyl pyrrolidone) (PVP) composite fiber precursors were prepared by the sol–gel assisted electrospinning. Subsequently, the M-type ferrite Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉ nanofibers with diameters about 120 nm were obtained by calcination of these precursors at different heat treatment conditions. The precursor and resultant Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉ nanofibers were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, energy-dispersive X-ray spectrometer and vibrating sample magnetometer. With the calcination temperature increased up to 1,000 °C for 2 h or the holding time prolonged to 12 h at 900 °C, the Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉ particles gradually grow into a hexagonal elongated plate-like morphology due to the dimensional control along the nanofiber length. These elongated plate-like particles will be linked one by one to form the nanofiber with a necklace-like morphology. The magnetic properties of the Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉ nanofibers are closely related to grain sizes, impurities and defects in the ferrite, which are influenced by the calcination temperature, holding time and heating rate. After calcined at 900 °C for 12 h with a heating rate of 3 °C/min, the optimized magnetic properties are achieved with the specific saturation magnetization 75.0 A m² kg⁻¹ and coercivity 426.3 kA m⁻¹ for the Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉ nanofibers.