Thermal analysis of CsH2PO4 nanoparticles using surfactants CTAB and F-68

A study concerned to thermogravimetric analysis is performed in cesium dihydrogen phosphate (CsH₂PO₄) that was synthesized, using cetyltrimethylammonium-bromide (CTAB), polyoxyethylene-polyoxypropylene (F-68) and mixture of (F-68:CTAB) with two mole ratio 0.06 and 0.12 as surfactant. The dehydration behavior of particles was studied using thermal gravimetric analysis and differential scanning calorimetric. Subsequently, the experimental results indicated that the first dehydration temperature in the range of 237–239 °C upon heating, the second peaks occur at temperature range 290–295 °C and overlapping in the thermogravimetric events is observed. The mass loss values are obtained in the range of 6.62–6.97 wt% that is less than reported theoretical value 7.8 wt%. These values show well compatibility of reaction CsH₂PO₄ to Cs₂H₂P₂O₇ with 3.92 wt% whereas mass loss value of CsH₂PO₄ to CsPO₃ is less than theoretical value 7.8 wt%. The activation energy of two steps dehydration are calculated using Kissinger equation for the samples synthesized via CTAB and (F-68) with minimum value mass loss 6.62% and maximum value mass loss 6.97%, respectively. The calculation results reveal that the reaction rate in the first step (CsH₂PO₄ → Cs₂H₂P₂O₇) is faster than the second step (CsH₂PO₄ → CsPO₃). The weight loss values of the samples demonstrate that existence of CTAB can be considered as effective factor which prevents more weight loss during the dehydration process.