Ultrahigh Molecular mass Polyethylene/ Carbon Nanotube CompositesCrystallization and melting properties

Ultrahigh molecular mass polyethylene (UHMMPE) is filled with carbon nano-tubes (CNTs) by solution in the presence of maleic anhydride grafted styrene-(ethylene-co-butylene)-styrene copolymer (MA-SEBS) as a compatibilizer. The UHMMPE/CNT composites crystallized from melt were prepared at a cooling rate of 20°C min^-1. The melting and crystallization behaviors of UHMMPE/ CNT composites were investigated by differential scanning calorimetry. The results showed that onset melting temperature (T _m) and degree of crystallinity (X _c) of UHMMPE/CNT composites crystallized from solution are higher than those from melt due to the larger crystalline lamellar thickness. The onset crystallization temperature (T _c) of UHMMPE/CNT composites tends to shift to higher temperature region with increasing CNT content in the composites. Tm and Tc of UHMMPE phase in UHMMPE/CNT composites decrease with the addition of MA-SEBS. Moreover, the crystallization rate of UHMMPE phase in UHMMPE/CNT composite is increased due to the introduction of CNTs. MA-SEBS acts as compatilizer, enhances the dispersion of CNTs in the UHMMPE matrix. Thereby, the crystallization rate of UHMMPE phase in UHMMPE/CNT composite is further increased with the addition of MA-SEBS. This revised version was published online in August 2006 with corrections to the Cover Date.