高炉渣非晶态含量的定量分析方法研究

通过X-ray衍射方法对高炉渣中非晶态与晶态的含量进行了定量分析研究。定量分析过程包括标准样品制备、配样与衍射以及数据处理分析。数据处理包括非晶态衍射峰及晶态峰在一定衍射角度内的积分、线性拟合与定量系数确定。提出了X-ray衍射方法所用的高炉渣标准样品的制备方法，包括100％非晶态标样和100％晶态标样。提出了由100％非晶态和100％晶态为标准样品时，高炉渣中非晶态含量的测定方法，适用于非晶态含量较高(>80%)的高炉渣的定量分析。结合数学处理和X-ray衍射结果，可得到原始高炉渣中非晶态含量和晶态含量，以及相应的比例系数，适用于非晶态含量高的高炉渣(>90%)。

Study on Quantificational Analysis Method for the Non-Crystalline Content in Blast Furnace Slag

Quantificational analysis method for the non-crystalline and crystalline contents in blast furnace slag was studied by means of X-ray diffraction. The process of quantificational analysis method includes standard samples preparation, samples preparation, X-ray diffraction measurement and data treatment. The data treatment includes integration areas of non-crystalline curve and crystalline peaks in certain diffraction angle range, linear fitting and quantificational coefficient determination. The preparation methods of standard samples for X-ray diffraction of blast furnace slag were proposed, including 100% crystalline sample and 100% non-crystalline sample. The 100% crystalline sample can be obtained by heating blast furnace slag for 12 h at 1 000-1 200 degrees C, and the 100% non-crystalline sample can be obtained by quenching the molten slag with enough water. The X-ray diffraction method of quantificational analysis of non-crystalline content in blast furnace slag was proposed with the 100% non-crystalline and 100% crystalline standard samples, and the quantificational coefficient can be obtained by linear regression on the integration areas of non-crystalline curve and crystalline peaks of X-ray diffraction in the 2-theta range 20 degrees-40 degrees. This method is suitable for the blast furnace slag with the non-crystalline content over 80%. The non-crystalline and crystalline contents of original blast furnace slag are obtained by combining the X-ray diffraction results and mathematical treatment, and this method is suitable for the blast furnace slag with the non-crystalline content over 90%, whose process includes preparing the 100% crystalline standard sample by heating blast furnace slag for 12 h at 1000-1200 degrees C, samples preparation with the 0.02 interval in the 0-0.1 mass ratio range of 100% crystalline to original slag, X-ray diffraction measurement of the samples prepared and data treatment using iterative linear regression. The quantificational analysis method for blast furnace slag can be applied to various kinds of blast furnace slag from different steel plants.