Oxidation kinetics of thin copper films and wetting behaviour of copper and Organic Solderability Preservatives (OSP) with lead-free solder |
| |
Authors: | Mauricio Ramirez Lothar HennekenSannakaisa Virtanen |
| |
Affiliation: | a Robert Bosch GmbH, Robert-Bosch-Strasse 2, 71701 Schwieberdingen, Germany b Chair for Surface Science and Corrosion, University of Erlangen-Nuremberg, Martensstrasse 7, 91058 Erlangen, Germany |
| |
Abstract: | The oxide formation on thin copper films deposited on Si wafer was studied by XPS, SEM and Sequential Electrochemical Reduction Analysis SERA. The surfaces were oxidized in air with a reflow oven as used in electronic assembly at temperatures of 100 °C, 155 °C, 200 °C, 230 °C and 260 °C. The SERA analyses detected only the formation of Cu2O but the XPS analysis done for the calibration of the SERA equipment proved also the presence of a CuO layer smaller than 2 nm above the Cu2O oxide. The oxide growth follows a power-law dependence on time within this temperature range and an activation energy of 33.1 kJ/mol was obtained. The wettability of these surfaces was also determined by measuring the contact angle between solder and copper substrate after the soldering process. A correlation between oxide thickness and wetting angle was established. It was found that the wetting is acceptable only when the oxide thickness is smaller than 16 nm. An activation energy of 27 kJ/mol was acquired for the spreading of lead free solder on oxidized copper surfaces.From wetting tests on copper surfaces protected by Organic Solderability Preservatives (OSP), it was possible to calculate the activation energy for the thermal decomposition of these protective layers. |
| |
Keywords: | Copper oxidation Soldering OSP Lead-free Final finish XPS |
本文献已被 ScienceDirect 等数据库收录! |
|