Crystallization behavior and microstructure of Fe75Co6Zr9B10 alloy
Authors:W.Q. YuY.M. Sun  Z. Hua
Affiliation:Key Laboratory of Functional Materials Physics and Chemistry of the Ministry of Education, Jilin Normal University, Siping 136000, Jilin, China
Abstract:Fe75Co6Zr9B10 amorphous alloy prepared by melt-spinning was annealed at various temperatures. The crystallization behavior and microstructure were investigated by differential thermal analysis (DTA), X-ray diffraction (XRD), transmission electron microscopy (TEM) and atomic force microscopy (AFM). The three exothermal peaks in the DTA curve of Fe75Co6Zr9B10 amorphous alloy correspond to the formations of α-Fe and α-Mn type phases, the growth of BCC-Fe volume fraction at the expense of α-Mn and residual amorphous phase and the precipitations of Fe3Zr, etc. intermetallic compounds, respectively. The second exothermic peak is not influenced by heating rate, but it shifts to a higher temperature region with increasing preannealing temperature of Fe75Co6Zr9B10 alloy. The α-Mn type phase is metastable and its lattice parameter determined by TEM is 0.8830 nm. AFM images show the development of surface morphology of alloy after annealing. The particle size increases with increasing annealing temperature.
Keywords:Crystallization behavior   Microstructure
本文献已被 ScienceDirect 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号