AES- und XPS-Untersuchungen zum Einflu? von Chrom, Nickel und Molybd?n auf das Korrosionsverhalten von rostfreien St?hlen in S?uren

Summary The alloys Fe17.8Cr, Fe16Cr2.4Mo and Fe18Cr14Ni2.5Mo (at%) were polarized in 0.5 mol/l H₂SO₄ or in 0.1 mol/l HC1 + 0.4 mol/l NaCl. The composition of the oxide layer and of the metallic layer beneath the oxide and the kinetics of the passive layer formation were determined by AES and XPS. In the active region, selective dissolution of Fe leads to an enrichment of Cr, Ni and Mo at the metal/electrolyte interface. In the passive region, the thickness of the rapidly formed passive layer is determined by the potential. The chromium content of the passive layer approaches a stationary, high value. The passive layer essentially consists of the anions O^2- and OH^– and of the cations of Cr, Fe, Mo, whereas Ni — and less pronounced Mo — are enriched below the layer.