| 掺杂对超导体(Tl1-x-yPbxMy)Sr2(Ca0.8Ln0.2)Cu2O7-δ(M=Sn4+或Sb5+, Ln=Y,La, Nd或Pr)性能的影响 |
| |
| 引用本文： | 张玉芬,周鼎元,郑香苗,林炳雄,唐有祺. 掺杂对超导体(Tl1-x-yPbxMy)Sr2(Ca0.8Ln0.2)Cu2O7-δ(M=Sn4+或Sb5+, Ln=Y,La, Nd或Pr)性能的影响[J]. 物理化学学报, 1990, 6(3): 259-262. DOI: 10.3866/PKU.WHXB19900302 |
| |
| 作者姓名： | 张玉芬 周鼎元 郑香苗 林炳雄 唐有祺 |
| |
| 作者单位： | Laboratory of Applied Physical Chemistry, Institute of Physical Chemistry, Peking University |
| |
| 摘 要： |
|
| 关 键 词： | 超导体 氧化物超导体 掺杂效应 |
| 收稿时间： | 1989-12-30 |
| 修稿时间： | 1990-02-12 |
Influence of Doping on Properties of Superconductor (Tl1-x-yPbxMy)Sr2(Ca0.8Ln0.2)Cu2O7-δ(M=Sn4+ or Sb5+, Ln=Y,La, Nd or Pr) |
| |
| Zhang Yu-Fen,Zhou Ding-Yuan,Zheng Xiang-Miao,Lin Bing-Xiong,Tang You-Qi. Influence of Doping on Properties of Superconductor (Tl1-x-yPbxMy)Sr2(Ca0.8Ln0.2)Cu2O7-δ(M=Sn4+ or Sb5+, Ln=Y,La, Nd or Pr)[J]. Acta Physico-Chimica Sinica, 1990, 6(3): 259-262. DOI: 10.3866/PKU.WHXB19900302 |
| |
| Authors: | Zhang Yu-Fen Zhou Ding-Yuan Zheng Xiang-Miao Lin Bing-Xiong Tang You-Qi |
| |
| Affiliation: | Laboratory of Applied Physical Chemistry, Institute of Physical Chemistry, Peking University |
| |
| Abstract: | Subramanian et al. found superconductivity at 80 K in Tl_(0.5)Pb_(0.5)Sr_2CaCu_2O_y sample with YBa_2 Cu_3 O_(7-δ)-like structure. However, there is unstable factor in the structure of the superconductor. Total plus valence is 12.5, and total minus valence is 14. The structure was further stabilized by partial substitution of Y, La, Nd orPr for Ca and Sn~(4+) or Sb~(5+) for (Tl, Pb), so that T_c was achieved above 100 K. For example, T_c is about 103 K in a sample with nominal composition (Tl_(0.4) Pb_(0.5)Sn_(0.2))Sr_2(Ca_(0.8)Y_(0.2))Cu_2O_(7-δ). During the preparation of superconductors, the temperature of samples was very slowly down after sintering, or samples were annealed at 500—700 ℃. The samples absorbed the oxygen during cooling, but no phase change occured. Appropriate amount of the oxygen made T_e higher. |
| |
| Keywords: | |
| 本文献已被 维普 等数据库收录！ |
| 点击此处可从《物理化学学报》浏览原始摘要信息 |
|
点击此处可从《物理化学学报》下载全文 |
|