Synthesis and Characterization of High-purity Aluminum Titanate with Water Quenching Method
Authors:SHEN Yang  RUAN Yu-Zhong  YU Yan
Institution:College of Materials Science and Engineering, Fuzhou University, Fuzhou, Fujian 350108, China
Abstract:High-purity aluminum titanate was synthesized via a water quenching method with waste-residue in the aluminum factory and industrial TiO2 as the main raw materials, which belongs to the comprehensive utilization of solid wastes. Compared with the conventional method, it can reduce synthesis temperature, effectively inhibit decomposition and raise the content of AT; the addition of tiny silicon powder can improve the sintering and optimize the properties of AT. The crystalline phase structure and microstructure of each sample were characterized with XRD and SEM methods; the content of each crystalline phase in each sample was confirmed with Rietveld Quantification method; the properties of each sample were also tested. The experimental results showed that No. 4 is the optimum specimen, with the corresponding mass ratio of Al2O3/TiO2 to be 1.27 and the content of AT of 97.2 wt%. The addition of optimum tiny silicon powder is confirmed to be 8wt%; its corresponding bulk density is 2.63 g/cm3, bending strength is 46.34 MPa, and the retention of one thermal vibration bending strength is 71.5%.
Keywords:aluminum titanate  water quenching method  aluminum waste-residue  tiny silicon powder
本文献已被 CNKI 维普 万方数据 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号