Vibrations and chemical states of iron ions in soda‐lime glasses determined by element‐specific X‐ray analyses

We systematically study medium‐range structures including more than three neighboring atoms around iron ions (Fe²⁺ and Fe³⁺) in soda‐lime glass samples with low iron oxide concentrations (M_Fe2O3) and a wide number ratio of Fe²⁺ to all iron ions (Fe²⁺/Σ_nFe). The precise medium‐range structures around iron ions in glass have not yet been revealed because of a lack of the appropriate measurement methods. To avoid this problem, we used element‐specific nuclear resonant inelastic scattering (NRIS) with synchrotron X‐rays to observe the vibrations of iron ions (⁵⁷Fe). The vibrations are related to medium‐range structures with more than three neighboring atoms and to the potential asymmetry and the coordination environment, around iron ions. The NRIS method has high sensitivity and can measure over a wide concentration range. Linear combination fitting of the X‐ray absorption fine structure spectra, which measures only the first neighbors but is a faster than using the NRIS method, was also used additionally. A systematically produced set of glasses with 0.015–5 wt% M_Fe2O3 and 0–0.85 Fe²⁺/Σ_nFe was measured with these methods. It was found that the soda‐lime glass possessed two different medium‐range structures with different iron ion valences (~2+ or ~3+), which were determined by the Fe²⁺/Σ_nFe, and that these structures were generated during production of the glass. Moreover, these medium‐range structures were the same from 0.015 to 5 wt% M_Fe2O3.