Conduction mechanism and the dielectric relaxation process of a-Se75Te25−xGax (x=0, 5, 10 and 15 at wt%) chalcogenide glasses

Se₇₅Te_25−xGa_x (x=0, 5, 10 and 15 at wt%) chalcogenide compositions were prepared by the well known melt quenching technique. Thin films with different thicknesses in the range (185–630 nm) of the obtained compositions were deposited by thermal evaporation technique. X-ray diffraction patterns indicate that the amorphous nature of the obtained films. The ac conductivity and the dielectric properties of the studied films have been investigated in the frequency range (10²–10⁵ Hz) and in the temperature range (293–333 K). The ac conductivity was found to obey the power low ω^s where s≤1 independent of film thickness. The temperature dependence of both ac conductivity and the exponent s can be well interpreted by the correlated barrier hopping (CBH) model. The experimental results of the dielectric constant ε₁ and dielectric loss ε₂ are frequency and temperature dependent. The maximum barrier height W_m calculated from the results of the dielectric loss according to the Guintini equation, and agrees with that proposed by the theory of hopping of charge carriers over a potential barrier as suggested by Elliott for chalcogenide glasses. The density of localized state was estimated for the studied film compositions. The variation of the studied properties with Ga content was also investigated. The correlation between the ac conduction and the dielectric properties were verified.