Visible light active hydrogen modified (HM)-n-TiO2 thin films for photoelectrochemical splitting of water

Visible light active hydrogen modified n-type titanium oxide (HM-n-TiO₂) thin films were synthesized by thermal oxidation of Ti metal sheet (Alfa Co. 0.25 mm thick) in an electric oven followed by incorporation of hydrogen electrochemically under cathodic polarization at ?1.6 V vs Pt. The photoresponse of the HM-n-TiO₂ was evaluated by measuring the rate of water splitting reaction to hydrogen and oxygen in terms of photocurrent density, J_p. The optimized electric oven-made n-TiO₂ and HM-n-TiO₂ photoelectrodes showed photocurrent densities of 0.2 mA cm^?2 and 1.60 mA cm^?2, respectively, at a measured potential of ?0.4 V vs Pt at illumination intensity of 100 mW cm^?2 from a 150 W xenon lamp. This indicated an eightfold increase in photocurrent density for HM-n-TiO₂ compared to oven-made n-TiO₂ at the same measured electrode potential. The band-gap energy of HM-n-TiO₂ was found to be 2.7 eV compared to 2.82 eV for electric oven-made n-TiO₂ and a mid-gap band at 1.67 eV above the valence band was also observed. The HM-n-TiO₂ thin film photoelectrodes were characterized using photocurrent density under monochromatic light illumination and UV–Vis spectral measurements.