γ-radiation-initiated emulsion polymerization of n-butyl acrylate and of methyl methacrylate

We have investigated the γ-radiation-initiated polymerization of n-butyl acrylate (BA) and of methyl methacrylate (MMA) in aqueous emulsions stabilized with sodium lauryl sulfate (SLS). The reaction rate, as measured by a nonabsolute thermocouple technique, varies as the square root of emulsifier concentration for both monomers. In the case of BA, the dose rate exponent of the reaction rate is 0.7 ± 0.3, whereas the corresponding value for MMA is approximately 0.4. The overall activation energy of the BA polymerization is close to zero, whereas for MMA a value of 4.8 ± 2.1 kcal/mole has been found. The poly(butyl acrylate) molecular weight is effectively independent of soap concentration and of dose rate but decreases as the reaction temperature is increased in the range 30–70°C. The general conclusion drawn from this work is that these radiation-induced emulsion polymerizations differ little from conventionally initiated systems insofar as the reaction kinetics are concerned. Poly(butyl acrylate-g-methyl methacrylate) copolymers have been prepared by a direct irradiation method involving a poly(butyl acrylate) prepolymer seed latex. Some physical properties of this material have been examined.